<p>I am using &quot;Pretty PETG&quot; along with PrusaSlicer's consecutive print mode.</p>
<p>What I am noticing is that upon finishing the first print, the printer hits <code>MINTEMP BED Fixed</code>. I'm not sure if it's immediate because I let the prints run overnight but I assume the bed cools down and then the error is hit.</p>
<p>I'm just starting to learn G-code and my initial thought was there's an errant bed temperature instruction but the only <code>M140 S0</code> instructions I see are in the <code>end_gcode</code> and near the bottom of the file. Maybe there a <code>goto</code> in G-code which may be running after <code>M140 S0</code> which then causes the <code>MINTEMP BED</code> issue? Perhaps there's something else going on?</p>

[{'answer_id': 14422, 'author': 'Trish', 'author_id': 8884, 'author_profile': 'https://3dprinting.stackexchange.com/users/8884', 'pm_score': 2, 'selected': False, 'text': '<p>0.2 mm and 0.4 mm are half the diameter, but the maximum flow is not just half: Flow scales with the area. The 0.4 mm nozzle has an area 4 times as the 0.2 mm one:</p>\n<p><span class="math-container">$\\frac{A_1} {A_2}=\\frac {0.2^2}{0.1^2}=4$</span></p>\n<p>You need to reduce <code>print speed</code> or the <code>volumetric flow</code> by this factor or make sure your printer can handle the increased flow by reducing the viscosity of the melt - for example by increasing the print temperature.</p>\n<p>Also note, that a 0.2 mm nozzle can\'t be operated with layer heights above 0.15\xa0mm.</p>\n'}, {'answer_id': 14428, 'author': 'Davo', 'author_id': 4922, 'author_profile': 'https://3dprinting.stackexchange.com/users/4922', 'pm_score': 1, 'selected': False, 'text': '<p>Here\'s where you change the speed in Prusa:</p>\n<p><a href="https://i.stack.imgur.com/FYF4a.png" rel="nofollow noreferrer"><img src="https://i.stack.imgur.com/FYF4a.png" alt="Changing Speed in Prusa" /></a></p>\n<p>As Trish said, you\'re likely trying to push too much material through too fast.</p>\n<p>Steps you can take:</p>\n<ol>\n<li>Increase print temp</li>\n<li>Decrease print speed</li>\n<li>Slice for thinner layers</li>\n<li>Don\'t forget to adjust your nozzle diameter and/or extrusion width(s) as well.</li>\n</ol>\n<p>I\'d personally start with increasing my print temp 10 degrees and cutting my print speed in half, as well as making sure I had 0.2 mm nozzle and extrusion widths.</p>\n'}, {'answer_id': 14430, 'author': 'cmm', 'author_id': 2082, 'author_profile': 'https://3dprinting.stackexchange.com/users/2082', 'pm_score': 0, 'selected': False, 'text': '<p>The discussion about slowing the print speed is important, but in my experience it is not at the root of the problem, and slowing down printing may make it worse.</p>\n<p>If ny &quot;heater&quot; you mean the complete hot-end, then I suspect you are jamming in the cooler part of the hot-end.  This cooler part is separated from the heater itself by the heat break, which is often a thin-walled metal tube.</p>\n<p>The hot side of the heat break is heated by the heater.  The cooler-end, the cool side of the heat break, is cooled by two things:</p>\n<ol>\n<li>cold filament being moved through it and</li>\n<li>airflow from the fan over the heat sink fins.</li>\n</ol>\n<p>It is heated by:</p>\n<ol>\n<li>Thermal conduction through the thin metal tube</li>\n<li>Convection airflow from the hot-end vertically and over the cooler-end</li>\n<li>Hot filament being pulled through the heat break during retraction.</li>\n</ol>\n<p>When you are printing with a smaller cross-section of extruded filament, the slicer program should adjust the flow rate and speeds based on the lesser volume of plastic extruded for a given pressure.  Unfortunately, this is less plastic, so the filament cools the cooler end of the heat break less than it would if the feed rate were higher.  As a result, the temperature of the cooler end goes up.  If there is insufficient airflow to keep the cooler side below the softening point of filament, the filament softens and jams inside the cooler end.</p>\n<p>Of course, if your jam actually is in the hot end, this discussion is not relevant.</p>\n<p>But, I have found with my Prusa i3m3 that I have had problems with jamming in the cooler end, especially when I printed filament with a higher melting temperature, ABS in this case.  I reduced the area of the airflow so that no air could pass through other than by passing over the heat sink fins, and the ABS printed correctly.</p>\n<p>All of 3D printing is a balance of one factor against another.  It is hard to lose, though, by increasing the cooler-end temperature.  All will seem well until you print something with a lower flow, or a higher retraction rate, or you try using a higher temperature for the same filament.  Then the jam can unexpectedly occur, or, perhaps worse, it can be an intermittent jam, or there can be a lot to sticktion, and printing becomes prone to gaps, or occasional under extrusion.</p>\n'}]
['https://3dprinting.stackexchange.com/questions/14435', 'https://3dprinting.stackexchange.com', 'https://3dprinting.stackexchange.com/users/23609/']