A series of multiarm star hydroxyl-terminated polyesters (MHPs) were synthesized through a "one-pot" method with di-trimethylolpropane as the core molecule, 2,2-dimethylolpropionic acid as the AB(2)-type monomer, epsilon-caprolactone, and monocarboxylic acids as modifiers. The influence of different monocarboxylic acids on the viscosities of polyesters and their 2K-PU films hardness was studied and it was found that MHPs prepared from lauric acid displayed the higher films hardness and lower viscosities. IR spectra of MHPs disclosed the ring-opening reaction between epsilon-caprolactone and hydroxyl groups occurred. H-1 NMR spectra demonstrated that the molecular structures of MHPs were irregular due to the multiplicity of reaction processes. The measured number-average molecular weights (M (n)) of MHPs were around 715-1854 g/mol with the PDI of 1.45-2.05. MHPs exhibited lower viscosities in the range of 3304-9060 mPa s at 100% solid contents and possessed lower intrinsic viscosities compared with linear polymers of similar molecular weight. The cured films of MHPs exhibited excellent impact resistance, adhesion, flexibility, and high hardness and displayed good thermal stability with 5% weight loss at 280A degrees C. The solution viscosities of MHPs were less than 450 mPa s at 80% solid contents, and the VOC contents of 2K-PU coatings obtained from MHPs were low to 300 g/L.