oral biofilm is the diverse microbial community found on the tooth surface , embedded in a matrix of polymers of bacterial and salivary origin . oral biofilm has been known to be closely related with the occurrence of oral disease.1 the formation of oral biofilm may lead to development of dental material surface biodegradation and secondary caries and periodontal inflammation , main reasons for the restoration replacement . in the process of plaque formation on solid substrate surfaces including teeth , implant and restorative materials , initial adhesion of the " early colonizers " to the surface is a critical step.1 - 3 oral streptococci have been known to bind to proteins such as alpha - amylase , proline - rich proteins and glycoproteins , and are recognized as early colonizers.4 streptococcus sanguis ( s. sanguis ) is thought to be one of the first bacterial species selectively adhere to teeth and colonize on saliva - coated teeth . this species appears in the human oral cavity after tooth eruption , and it becomes a normal inhabitant of the human mouth.4,5 numerous factors have been identified to influence oral biofilm formation such as surface roughness and surface free energy.6,7 microscopic examination of early plaque formation on teeth showed the adhesion of the initial colonizing bacteria along cracks and pits in enamel , suggesting the influence of surface structure on bacterial adhesion.3 it is evident that implant and restorative materials have different surface characteristics . various affinities of oral bacteria adhesion have been reported for different materials including titanium.7 - 10 resin composites have been widely used for operative , esthetic , and prosthodontic treatments.3,8 dental ceramic materials also applied to broad range of clinical practice . especially , zirconia has been introduced to improve esthetics for natural teeth and implant prostheses because of its biocompatibility , high resistance to wear and fracture by fatigue loading.10 - 12 the purpose of this study is to compare and characterize biofilm formation on commonly utilized restorative materials such as composite resin , titanium and zirconia . resin composite was dispensed from a syringe into a mold , and then light - cured for 30 seconds from the top and the bottom side respectively with a light curing unit ( shinwon dental , seoul , korea ) . commercially pure titanium ( cp - ti ) bars were machined into discs and 3y - tzp powder was die - pressed into disks and then isostatically pressed at 140 mpa . three kinds of 12 mm diameter disc specimens were gradually polished and finished with 1 m diamond paste to acquire mirror - like surface . the average surface roughness ( ra ) and topography were measured by the confocal laser microscope ( zeiss , germany ) . the static water contact angle of each surface of specimen was measured with a phoenix 300 contact - angle meter ( surface electro optics , korea ) at room temperature . s. sanguis 804 ( nctc 10904 ) was maintained in sterile trypticase soy broth ( bd diagnostics , md , usa ) supplemented with yeast extract ( bd diagnostics ) . prior to seeding , sterilized specimens were placed into a 24-well culture plate and were incubated with saliva for 2 hours at 37. the saliva was collected from one healthy donor who did not show any active carious lesions or periodontal diseases and sterilized by filtration devices with pore sizes 0.2 m ( millipore , ma , usa ) . after washing with pbs , bacteria were seeded onto the specimens at a density of 110 bacteria / cm . the crystal violet ( cv ) assay was performed to determine the total amount of biofilm . then , wells were washed once with pbs and the plates were air - dried . the biofilm was stained using 1% crystal violet solution ( sigma - aldrich , md , usa ) , followed by 10 minutes incubation time at room temperature . then , the excess of unbound dye was removed by washing the plates with deionized water . the bound cv was extracted with destaining solution ( 80% ethanol , 20% acetone ) . the amount of biofilm was measured at optical density of 595 nm using a microplate reader ( bio - rad laboratories , ca , usa ) . the background staining was corrected by subtracting the mean value for cv bound to negative controls . the fluorescence resazurin ( 0.75 g / ml , sigma , md , usa ) was used to determine the quantity of viable adherent bacteria . bacterial suspension with resazurin was incubated on each specimen at 37 for 150 minutes . after washing with pbs , fluorescence intensities were recorded by detection reader ( fluostar optima ; mbg labtech , offenburg , germany ) at wavelengths of 540 nm excitation and 590 nm emissions . s. sanguis attachment and morphology were also assessed after 4 hours culture by scanning electron microscopy ( jeol , tokyo , japan ) . after washing twice in the 0.1 m phosphate buffer , bacteria are post fixed with 1% oso4 in saturated hgcl2 . after dehydration in graded ethanol , bacteria are critical point dried and coated with gold by ion sputtering for 2 minutes . statistical analysis was performed using one - way analysis of variance ( anova ) and the tukey - kramer multiple comparison test was used for post hoc analysis . resin composite was dispensed from a syringe into a mold , and then light - cured for 30 seconds from the top and the bottom side respectively with a light curing unit ( shinwon dental , seoul , korea ) . commercially pure titanium ( cp - ti ) bars were machined into discs and 3y - tzp powder was die - pressed into disks and then isostatically pressed at 140 mpa . three kinds of 12 mm diameter disc specimens were gradually polished and finished with 1 m diamond paste to acquire mirror - like surface . the average surface roughness ( ra ) and topography were measured by the confocal laser microscope ( zeiss , germany ) . the static water contact angle of each surface of specimen was measured with a phoenix 300 contact - angle meter ( surface electro optics , korea ) at room temperature . s. sanguis 804 ( nctc 10904 ) was maintained in sterile trypticase soy broth ( bd diagnostics , md , usa ) supplemented with yeast extract ( bd diagnostics ) . prior to seeding , sterilized specimens were placed into a 24-well culture plate and were incubated with saliva for 2 hours at 37. the saliva was collected from one healthy donor who did not show any active carious lesions or periodontal diseases and sterilized by filtration devices with pore sizes 0.2 m ( millipore , ma , usa ) . after washing with pbs , bacteria were seeded onto the specimens at a density of 110 bacteria / cm . the crystal violet ( cv ) assay was performed to determine the total amount of biofilm . then , wells were washed once with pbs and the plates were air - dried . the biofilm was stained using 1% crystal violet solution ( sigma - aldrich , md , usa ) , followed by 10 minutes incubation time at room temperature . then , the excess of unbound dye was removed by washing the plates with deionized water . the bound cv was extracted with destaining solution ( 80% ethanol , 20% acetone ) . the amount of biofilm was measured at optical density of 595 nm using a microplate reader ( bio - rad laboratories , ca , usa ) . the background staining was corrected by subtracting the mean value for cv bound to negative controls . the fluorescence resazurin ( 0.75 g / ml , sigma , md , usa ) was used to determine the quantity of viable adherent bacteria . bacterial suspension with resazurin was incubated on each specimen at 37 for 150 minutes . after washing with pbs , fluorescence intensities were recorded by detection reader ( fluostar optima ; mbg labtech , offenburg , germany ) at wavelengths of 540 nm excitation and 590 nm emissions . s. sanguis attachment and morphology were also assessed after 4 hours culture by scanning electron microscopy ( jeol , tokyo , japan ) . after washing twice in the 0.1 m phosphate buffer , bacteria are post fixed with 1% oso4 in saturated hgcl2 . after dehydration in graded ethanol , bacteria are critical point dried and coated with gold by ion sputtering for 2 minutes . statistical analysis was performed using one - way analysis of variance ( anova ) and the tukey - kramer multiple comparison test was used for post hoc analysis . the surface of resin composite was significantly rougher than that of titanium and zirconia although final polishing condition was the same ( table 1 ) . however , all tested specimens demonstrated mean surface roughness values below 0.2 m , and were therefore classified as smooth clinically . table 1 also reports the mean values of water contact angles measurements , ranging between 54.2 and 75.1. the contact angle of titanium and zirconia were similar , however resin specimen showed significantly lower contact angle . it can be seen that there is a difference among the number of bacteria on resin , titanium and zirconia . as observed by sem , biofilm colonies were more abundant on resin in comparison with those of titanium and zirconia ( fig . 1 ) . a further analysis was performed to investigate the number of attached bacteria on each specimen quantitatively . the result of relative fluorescence intensities resulting from resazurin reduction also demonstrated that viable s. sanguis bound on each specimen . the fluorescence intensity on titanium was not significantly different from that on zirconia ( fig . oral biofilm formation on the surface of restorative and implant materials leads to secondary caries formation and affects healing process negatively . therefore , it is important to investigate the initial bacteria adhesion on the surface of biomaterials . the initial colonizers , including s. sanguis , s. gordonii and s. oralis , adhere to the pellicles on solid surfaces by several factors , namely , electrostatic and hydrodynamic interactions , thermodynamic parameters and adhesion - receptor interactions.5,11 this event leads to subsequent adhesion of cariogenic microorganisms such as s. mutans and periodontal pathogens , which may induce gingival and periodontal inflammation.13,14 the sem examination confirmed that s. sanguis can bind directly to the surface of resin , titanium and zirconia . however , adhesion of the total and viable bacteria on resin is significantly higher when evaluated by crystal violet staining and fluorometic quantification , respectively . surface roughness has been regarded as one of the most important factors . with regard to the influence of surface roughness on biofilm formation , rougher surface results to the increased adhesion of bacteria.6,7 in this study , we tried to eliminate the difference of roughness by polishing 1 m diamond paste . although , the roughness of resin showed similar level with previous report,3 it is still higher than the roughness of titanium and zirconia . previous report showed that protein adsorption and bacterial adhesion in vivo are primarily determined by a threshold surface roughness of 0.2 m , therefore ra less than threshold level appears to have a negligible effect.15,16 however , correlation of surface roughness and bacterial adhesion could be observed this in vitro study . to confirm this result when comparing between titanium and zirconia , our results demonstrated that there is no significant difference on s. sanguis adhesion . this contrasts with previous reports9,17 showing that fewer bacteria adhered to zirconia in comparison with titanium of a similar surface roughness in vivo . previous studies compared the bacterial adhesion using titanium and zirconia with rough surface which showed approximately 0.73 m of ra . to confirm , a further study will be performed to compare the bacterial adhesion according to the different level of roughness on biomaterials including titanium , zirconia and resin . surface hydrophobicity is another crucial element for influencing the bacterial adhesion.6,15 s. sanguis is highly hydrophobic microorganism . it is possible that the difference of bacterial adhesion is derived from the surface hydrophobicity . however , hydrophobicity of resin surface is lower than that of titanium and zirconia and more bacterial adhesion was observed . this observation may be the result from the difference of surface roughness even though all the specimens have surface roughness less than 0.2 m . the additional physic - chemical characteristics including crystallinity have been shown to affect biofilm formation in vivo and in vitro.7,18 it is unreasonable to conclude that difference in bacterial adhesion is entirely attributed to different surface roughness in this study . further studies are needed to investigate the bacterial adhesion on the various biomaterials not only by roughness but also by additional surface characteristics . within the limitations of this study , composite resin has a significantly higher susceptibility to adhere the initial colonizer , s. sanguis , than titanium and zirconia under the same polishing condition . the amount of both total and viable bacteria on resin was higher than those on titanium and zirconia .
purposethe aim of this in vitro study was to investigate the adhesion of initial colonizer , streptococcus sanguis , on resin , titanium and zirconia under the same surface polishing condition.materials and methodsspecimens were prepared from z-250 , cp - ti and 3y - tzp and polished with 1 m diamond paste . 
 after coating with saliva , each specimen was incubated with streptococcus sanguis . scanning electron microscope , 
 crystal violet staining and measurement of fluorescence intensity resulting from resazurin reduction were performed for quantifying the bacterial adhesion.resultssurface of resin composite was significantly rougher than that of titanium and zirconia , although all tested specimens are classified as smooth . 
 the resin specimens showed lower value of contact angle compared with titanium and zirconia specimens , and had hydrophilic surfaces . 
 the result of scanning electron microscopy demonstrated that bound bacteria were more abundant on resin in comparison with titanium and zirconia . when total biofilm mass determined by crystal violet , absorbance value of resin was significantly higher than that of titanium or zirconia . 
 the result of relative fluorescence intensities also demonstrated that the highest fluorescence intensity was found on the surface of resin . 
 absorbance value and fluorescence intensity on titanium was not significantly different from those on zirconia.conclusionresin specimens showed the roughest surface and have a significantly higher susceptibility to adhere streptococcus sanguis than titanium and zirconia when surfaces of each specimen were polished under same condition . 
 there was no significant difference in bacteria adhesion between titanium and zirconia in vitro .