titanium has been used as standard material in dental implantology for implants and abutments due to its excellent mechanical and biological properties . nevertheless , there are some esthetical limitations for metal - based implant supported reconstructions because of its lacking translucency and dark grey margins.1,2 therefore , yttria - stabilized zirconia has been established as a suitable material for the basis of prosthetic superstructures on dental implants.3,4 this polycrystalline ceramic offers best mechanical resistance , biological advantages like reduced plaque - accumulation combined with a satisfying esthetical performance.5 the fabrication of such restorations via computer - aided design and computer - aided manufacturing ( cad / cam ) bears some advantages like an economic processing and advanced marginal precision6 where quality is affected by processing routes like centralized or in - lab production7 and different milling strategies.8 implant - supported superstructures could be subdivided into screw - retained or cement - retained restorations . in literature , there is actually no consent which of these fixing techniques provides better mechanical or biological clinical performances and some advantages and disadvantages were still controversial . cement - retained reconstructions provide better esthetics , functional occlusions , clinical operability and lower costs.9,10 advantages of screw - retained superstructures are better reparability ( for instance in case of loosening of the abutment - screw or chippings of the veneering ceramic ) and cleanability due to their retrievability.11 furthermore , there are possibly lower peri - implantitis rates because there is no cement - induced irritation of peri - implant tissues.12 however , during a 5-year observation period the survival rates of screw - retained and cement - retained implant crowns were similar.13 to maintain the advantages of retrievability also for cement - retained superstructures provisional or semi - permanent luting agents can be used.14 otherwise the opacity of provisional luting agents may lead to a reduced esthetical performance and cement washout can induce debonding of the restoration.9 modern semi - permanent cements from different companies developed for the luting especially on implant abutments provide higher levels of translucency and transparency . however , data regarding the retentiveness levels of semi - permanent luting agents are actually rare . there is the possibility of individual angulation and resulting higher fracture resistances,15 advanced esthetics of the surrounding soft tissues due to a better support via a correct emergence profile,16 a better removability of remnants of cements17 and the reduction of technical complications like retention - loss or screw loosening.18,19 furthermore , there is the opportunity for enhancing retentiveness of cement - retained copings due to optimized geometries20,21 where retention is more affected by taper and height than by width or total surface of the abutment.22,23 cementation type implant restorations sometimes need recementationand to clean the remaining cements in an ultrasonic bath containing alcohol and sandblasting with aluminium oxide for zirconia copings prior to cementation on implant abutments were performed.24,25 etching , burnout or manual cleaning ( we think clinically the most common technique ) with curettes or similar instruments are other known methods for removing provisional cement before re - cementing of the copings . but to the author 's knowledge , there is only one study available that evaluates the effect of different cleaning methods on retentiveness of temporarily cemented casted ( no zirconia ) copings after re - cementation but for cleaning of the abutments , not the inner surface of the copings ; and in that study , airborne particle abrasion was the most effective technique.26 furthermore , sandblasting of zirconia copings is seen critically regarding the influence of the mechanical integrity of the copings by some authors,27,28 so that it is still unclear what cleaning method could be truly recommended for debonded temporarily cemented zirconia copings . the aim of this study was to evaluate the retentiveness levels of single zirconia copings on titanium abutments cemented with a provisional ( tempbond ne , kerr , hamm , germany ) and a semi - permanent ( telio cs cem implant , ivoclar vivadent , ellwangen , germany ) luting agent in dependence on three different abutment geometries ( prefabricated , customized - long and customized - short ) . furthermore , the resulting retentive force of temporarily cemented zirconia copings on titanium abutments depending on three different cleaning methods ( manual , manual in combination with ultrasonic bath and sandblasting ) prior to re - cementation was investigated . finally , a scanning electron microscopy ( sem ) analysis of the inner surface of the zirconia copings after the different cleaning techniques was performed . for evaluation of the retentiveness of zirconia copings two series of uni - axially pull - out tests were performed : a ) regarding the influence of three different geometries in combination with two different luting agents ( n = 60)(fig . 1 show all conducted investigations ) and b ) regarding the influence of three different cleaning techniques ( n = 52 ) after debonding prior to re - cementation of the copings . titanium ankylos implants ( dentsply implants manufacturing gmbh , mannheim , germany ) with a diameter of 3.5 mm and a length of 11 mm were embedded strictly vertical with the help of a parallelometer in a block of autopolymerizing acrylic resin ( palavit g , heraeus kulzer , hanau , germany ) . an individually designed retainer made of stainless steel three different types of titanium abutments were used . in the first series pre - fabricated abutments with a height of 7.5 mm and a taper of 5.7 ( ankylos regular c , dentsply implants manufacturing gmbh , mannheim , germany ) the customized abutments and all fabricated zirconia copings were designed using the cad system cercon art 3.2.2 ( degudent gmbh , hanau , germany ) and fabricated by compartis ( degudent ) . all of the abutments were fixed on the implants with a torque of 15 ncm . the design of the zirconia copings included special hooks on the top of the copings to allow the application of a pull - out force later on . the copings were randomly assigned to subgroups for the various luting agents and cleaning methods . evaluated luting agents for the retentive forces of zirconia copings were a provisional ( tempbond ne , kerr , hamm , germany ) and a semi - permanent ( telio cs cem implant , ivoclar vivadent , ellwangen , germany ) cement in combination with three different abutment designs . for the evaluation of the influence of the cleaning method ( manually using a curette and gauze , manually in combination with ultrasonic bath ( isopropyl alcohol , 30 , 15 min ) and sandblasting with 110 m aluminium oxide particles ( 2 bar , 15 s , held at distance of 10 mm ) only the provisional cement ( tempbond ne , kerr , hamm , germany ) on prefabricated titanium abutments ( dentsply implants manufacturing gmbh , mannheim , germany ) was used for both , primary cementation and re - cementation after dislodgement . the provisional luting agent tempbond ne is a non - eugenol zinc - oxide cement . both agents were mixed according to the manufacturer 's instructions at room temperature ( 23 ) . telio cs was delivered in self - mixing cartridges , for tempbond ne the mixture ratio of 1:1 for base and catalyst paste was weighted with a tolerance limit of 0.1 mg . after seating of the copings onto the abutments a weight of 2.0 kg was applied to the copings for 5 min . when using the composite for luting additionally uv light was applied for 40 s. before performing the pull - out test each specimen of all series was letting rest for 24 h. each coping was pulled off from the abutment in axial direction using a specially fabricated device ( fig . 2 ) with a universal testing machine ( zwick z007 , zwick gmbh & co , ulm , germany ) at a crosshead speed of 5 mm / min and the dislodgement strength was recorded in newton using the testing software ( testxpert2 , zwick gmbh & co , ulm , germany ) . the inner surface of one specimen per cleaning technique and one untreated coping as reference was evaluated with a sem ( quanta 200 , fei , hillsboro , or , usa ) at a working distance of 10 mm . statistically significant differences were determined via two - way anova for the test variables " abutment geometry " and " luting agent " and via one - way anova for " cleaning technique " . all tests were accomplished using the software sas 9.2 ( sas institute inc . , cary , nc , usa ) . significant interactions between abutment geometries and luting agents could be demonstrated ( p<.002 ) . for the pre - fabricated abutments the evaluated retentiveness levels of the luting agents showed no significant difference ( p=.2495 ) . values for telio cs differed from 44.92 to 104.91 n and for tempbond ne from 62.83 to 111.93 n. means with standard deviations and the corresponding 95% confidence intervals are demonstrated in table 1 and fig . 4 . the removal forces of customized - short abutments ranged for telio cs from 71.87 to 141.00 n. the respective values for the provisional cement tempbond ne were significantly inferior to those of the semi - permanent luting agent ( 11.20 to 60.45 n , p<.0001 ) . means with standard deviations and corresponding 95% confidence intervals the effect of the luting agent was inverted relatively to the values of the customized - short series . the retentive strength of tempbond ne ranged from 100.5 to 174.26 n and was significantly superior ( p<.0008 ) to the retentiveness of telio cs ( 52.90 to 117.64 n ) . means with standard deviations and 95% confidence intervals are shown in table 1 and fig . so it can be stated that the effect of the luting agent is not consistent through the series of different abutment geometries . a significant impact of the cleaning technique on the required dislodgement forces could be shown ( p<.001 ) . all specimens within these series the reference series ( primary cementation ) showed values of retentive forces from 50.36 to 111.93 n. after manual cleaning the retentive strength ranged from 33.66 to 79.29 n. when manual and ultrasonic cleaning was combined increased values of 57.72 to 129.28 n were necessary for dislodgement . after sandblasting of the copings removing forces of 44.49 to 90.82 n have to be applied . only the combination of manual and ultrasonic cleaning enables retentive forces of tembbond ne after re - cementation comparable to primary cementation ( no significant difference , p=.3224 ) . both , cleaning with hand instruments ( p=.003 ) and sandblasting ( p=.0348 ) showed significantly lower retention forces after re - cementation than the reference group . all means , standard deviations and 95% confidence intervals are shown in table 2 and fig . 5 . the scanning electron micrograph of the untreated coping ( before cementation ) shows distinct grinding marks ( fig . the specimens show remnants of the cement and scratch marks of the used hand instruments ( fig . 6b ) . when additionally an ultrasonic bath was used , the surface quality seemed to be more homogenous and cement particles were nearly eliminated ( fig . after sandblasting all cement particles were completely removed , surface quality could be rated as very homogenous with a slightly increased surface roughness ( fig . in this study , uni - axial pull - out tests were performed to evaluate retention forces of zirconia copings cemented with a provisional ( tempbond ne ) and a semi - permanent ( telio cs ) luting agent on implant abutments with varying geometries ( pre - fabricated , customized - long , customized - short ) and different cleaning techniques ( manually , manually and ultrasonic bath , sandblasted ) prior to re - cementation . in this study , values for provisionally or semi - permanently cemented zirconia copings on implant abutments between 29.36 n ( customized - short abutment , tempbond ne ) and 131.70 n ( customized - long abutment , tempbond ne ) were revealed . these values were consistent to another study investigating retentiveness levels of cobalt - chromium and zirconia copings on implant abutments with varying tapers and surface roughness cemented with definitive and provisional luting agents.21 another study investigating the retention of zirconia copings on zirconia abutments revealed also comparable values for tempbond ne ( around 100 n).25 for customized - long abutments tempbond ne offered the highest retention strength ( 131.70 n ; telio cs : 88.25 n ) . but attachment surface and taper seemed to be crucial for the mechanic retention of the provisional luting agent . another study revealed that retention forces for implant - retained single crowns cemented with tempbond ne was significantly increased by additionally prepared circumferential grooves , supporting the hypothesis that provisional luting is critically effected by abutment geometries.29 however , retention forces when the semi - permanent luting with telio cs was performed were consistent through all series between 75.61 and 106.45 n , also when height of the abutments was significantly reduced ( customized - short ) . but it has been shown that height of the abutment could significantly influence the retention for of single crowns.30 for customized - short series retentiveness levels of temp bond ne were dramatically reduced ( 29.36 n ) . maybe a certain adhesive effect of the resin - based semi - permanent telio cs compensates unfavorable abutment geometries . however , some specimens of telio cs were found not adequately hardened after dislodgement although a 24 h phase of drying before the pull - out tests were strictly applied . this could be a possible explanation for the wide range of values and its respective standard deviations ( table 1 ) . but all processes within this study were performed strictly according to the manufacturer 's instructions ( calibration of the investigators was done during some pilot experiments ) . especially variations of the manual mixing processes had to be avoided as far as possible.31 it is known , that besides internal and marginal accuracy of the restorations also the cement space is a determining factor for retentive strength.32 some studies postulate an insufficient polymerization of resin - based cements when film thickness amounts below 20 m.33 however , manufacturers of modern luting agents predict film thicknesses around 10 m due to a good flowability , for example for telio cs . a recent study demonstrated that retention of implant - supported crowns was significantly increased for a film thickness of 15 m relatively to 50 m , especially for resin - based cements.34 in our study , customized - long abutments showed better retentiveness levels than the pre - fabricated ones despite of lower heights ( 6.79 mm vs. 7.5 mm ) . recently , it has been demonstrated that retentiveness levels were significantly affected by abutment heights only when the difference exceeded a moderate amount.35 maybe the better retention of the customized abutments was caused by the smaller taper degree ( 4.8 vs. 5.7 ) as it was demonstrated in other studies evaluating the retention forces of implant - retained crowns in dependence of different abutment geometries.21,36 but an increased degree of taper seemed to be more effective for solid cements than for provisional luting agents . however accordingly to our previous study it was demonstrated that the provisional luting agent ( tempbond ne ) was more sensitive regarding retentive strength for varying taper degrees than the semi - permanent cement ( implantlink , detax , ettlingen , germany).21 another co - factor for better retention forces on customized abutments might be a better precision of fit than for pre - fabricated ones . customized abutments showed less degree of rotation ( < 3)18 between abutment and implant interface than prefabricated ones ( > 5)37 but a precise congruence is a crucial factor for the integrity of the whole construction and respective retentiveness levels of the copings.36,38 due to possible misfit of zirconia - based abutments caused by shrinking processes during sintering , titanium abutments were used in this study . furthermore , a metal - to - metal interface seemed to be preferable because the increased hardness of zirconia abutments can lead to abrasion of the metal surface of the implant due to micro movements at the interface.39 for evaluation of the efficacy of the cleaning methods only the series of tempbond ne was chosen because remnants of telio cs were not residual on the copings and could be easily removed in toto from the abutment , which can be seen as clinical advantage because easy and complete removability is useful to prevent peri - implantitis . the investigated cleaning methods were chosen after some pilot - series that formerly included the burnout and edging method . the reference series ( dislodgement after primary cementation ) revealed values of retentive strength around 78.61 n. after manual cleaning with hand instruments lowest levels of retention ( 54.74 n ) were measured after re - cementation . as seen on sem ( fig . this is consistent to the results of a study investigating the influence of implant abutment cleaning techniques on retentive strength of zirconia copings.26 the sandblasted copings showed the most homogenous surfaces free of cement 's remnants ( fig . 6d ) , as it was also demonstrated for the cleaning of implant abutments.26 however , sandblasting prior to re - cementation ( retentive strength : 61.82 n ) leads to values that were better than after manual cleaning but also significantly inferior to those of the reference series . maybe there was a relevant air abrasion , causing a reduced precision of fit that lead to a less retentive force due to a thicker cement film another possible explanation regarding this phenomenon could be that an equalization of the inner surface due to air abrasion reduced the stiction of the cement particles . results of previous studies regarding the impact of sandblasting on retention forces are inconsistent : it has been demonstrated that there was no significant effect for improving the retentive strength of provisional luting agents25 but otherwise sandblasting has significantly improved retention strength of implant retained single crowns cemented with various provisional and permanent luting agents.35 in addition , the influence of sandblasting on the mechanical integrity of zirconia copings is still unclear and is discussed critically by some authors.27,28 to the author 's knowledge comparable investigations are rare . in one study , sandblasting was combined with ultrasonic cleaning for 3 min.40 in our study manual cleaning was combined with an ultrasonic bath for 15 min . the crown retention after combined manual and ultrasonic cleaning was slightly but not significantly increased relatively to dislodgement forces after primary cementation . on the respective sem ( fig . furthermore , it seemed that some zirconia crystallites were separated from the surface , possibly leading to an enlargement of the contact area and better retention . the uni - axial pull - out test allows functional evaluation of various impact factors on retention forces of dental restorations . in this study , this must be seen critically regarding the transferability of our in vitro results directly to clinical situations . it has been shown that thermocycling could be a crucial factor for determining the retentive strength of tempbond ne.21,25,30 the uni - axial test is also limited in representing adequate clinical situations because naturally multidirectional forces were applied on restorations and implants during mastication or bruxism . considering the conditions and limitations of this in vitro study , the following conclusions can be drawn : the provisional luting agent ( tempbond ne ) was more affected by different heights and tapers of the abutment . therefore , semi - permanent luting agents should be used when adequate geometries of the abutments can not be realized . the combination of manual and ultrasonic cleaning for temporarily cemented , debonded zirconia copings seemed to be an adequate and clinically feasible procedure to obtain retention forces for re - cementation comparable to primary luting .
purposeto evaluate the effects of different abutment geometries in combination with varying luting agents and the effectiveness of different cleaning methods ( prior to re - cementation ) regarding the retentiveness of zirconia copings on implants.materials and methodsimplants were embedded in resin blocks . 
 three groups of titanium abutments ( pre - fabricated , height : 7.5 mm , taper : 5.7 ; customized - long , height : 6.79 mm , taper : 4.8 ; customized - short , height : 4.31 mm , taper : 4.8 ) were used for luting of cad / cam - fabricated zirconia copings with a semi - permanent ( telio cs ) and a provisional cement ( tempbond ne ) . 
 retention forces were evaluated using a universal testing machine . 
 furthermore , the influence of cleaning methods ( manually , manually in combination with ultrasonic bath or sandblasting ) prior to re - cementation with a provisional cement ( tempbond ne ) was investigated with the pre - fabricated titanium abutments ( height : 7.5 mm , taper : 5.7 ) and sem - analysis of inner surfaces of the copings was performed . 
 significant differences were determined via two - way anova.resultssignificant interactions between abutment geometry and luting agent were observed . 
 tempbond ne showed the highest level of retentiveness on customized - long abutments , but was negatively affected by other abutment geometries . 
 in contrast , luting with telio cs demonstrated consistent results irrespective of the varying abutment geometries . 
 manual cleaning in combination with an ultrasonic bath was the only cleaning method tested prior to re - cementation that revealed retentiveness levels not inferior to primary cementation.conclusionno superiority for one of the two cements could be demonstrated because their influences on retentive strength are also depending on abutment geometry . 
 only manual cleaning in combination with an ultrasonic bath offers retentiveness levels after re - cementation comparable to those of primary luting .