hermann suggested in 1920 that materials containing calcium hydroxide had an important use as bases and cavity liners2,18 . their indications include favoring pulp healing after injury by caries and/or operational procedures as well as protecting the pulp against the penetration of components of restorative materials and oral substances11,1618 . additionally , calcium hydroxide cements have been largely used in deep cavities because of their capacity to stimulate dentin formation1,5,6,8,11,14 . more recently , manufacturers have produced resin - based calcium containing materials with superior physical properties when compared to cements without resin components . although hard - setting calcium hydroxide cements may induce the formation of dentin bridges , they are not likely to provide an effective long - term seal when facing bacterial challenge . within a few years , the majority of mechanically exposed and capped pulps show infection and necrosis caused by microleakage of such capping materials and tunnel defects in the dentin bridges13,17 . strength properties of these cements are relatively low and solubility is relatively high in many instances15 . several cases are mentioned in the literature in which base / liner materials , after some time , are not capable to remain stable under restorations , leaving the cavity without protection and the restoration without support , which may be caused by the material 's dissolution or water sorption . this may occur when the material get in contact with either dentinal fluid , which is more common in freshly prepared cavities , or aqueous medium , that is , due to marginal infiltration or hydrolytic decomposition4,9,10,13 . these points suggest that the lining permanence between the tooth and the restoration is of particular importance . moreover , material solubilization , or its water sorption , may be directly related to the loss of its properties . in addition , the resistance of calcium hydroxide cements to disintegration has been an important criterion to evaluate the quality of these materials3 . it is unknown whether relative newer types of resin containing calcium hydroxide cements will act as a permanent barrier . based on these data , pulp capping with resin - based cements may look promising , but , in fact , more research is necessary to provide a valuable confirmation13 . taking these aspects into account , it seems interesting to evaluate the behavior of different calcium hydroxide cements regarding their water sorption and solubility properties , in order to show possible alterations that may be present after some time , which reduce their effectiveness . three commercial brands of calcium hydroxide cements were evaluated : one resin - modified light curing cement and two chemically activated cements that are mainly used in the brazilian clinical practice . the american dental association 's specification # 8 ( zinc phosphate cement solubility ) was adopted with a few small modifications to design the methodology used in this study : the solubility tests used distilled water rather than oral fluids for immersion of specimens , and the specimens were stored for 1 week3 . for the solubility tests , 5 disc - shaped specimens ( 20 mm diameter x 1.5 mm thick ) of each material ( biocal , dycal and hidro c - figure 1 ) were prepared ( figure 2 ) . the mixing of the two pastes of each material was carried out according to the manufacturers ' instructions , using standardized techniques , in a 1:1 weight proportion , in a room with climate - controlled conditions ( 5010% humidity and 232c ) . for fabrication of the specimens , a metallic ring matrix with a 20-mm - diameter and 1.5-mm - thick central perforation the perforation was filled with the calcium hydroxide cement using a centrix injector and the matrix was covered with a polyester strip and a glass plate , which were maintained under finger pressure until the complete setting of the material ( figures 3 and 4 ) . a dental floss was embedded in each disc in order to help handling the specimens ( figure 5 ) . after 24 h , the specimens were weighed on a precision scale , dehydrated in an oven at 37c for 1 h and weighed again . immediately after weighing , the discs were stored in individual flasks containing 50 ml of distilled water at 37c during 1 week ( figure 6 ) , and weighed and dehydrated again , as mentioned above , and subjected to a new weighing . the loss of soluble material was obtained from the difference between the initial and the final drying mass of each disc , discounting the mass of the ring - dental floss unit . the water sorption was obtained from the difference between the wet and the dry mass of each disc , and from another weighing after 1 week immersion in water . the water sorption and solubility values obtained for each material were analyzed statistically by two - way anova and tukey 's tests at 5% significance level . biocal showed the lowest water sorption ( 2.15% ) and differed significantly from the other materials . dycal showed intermediary water sorption values ( 5.49% ) and hidro c showed the highest values ( 8.27% ) ( table 1 ) different letters indicate statistically significant differences ( p<0.05 ) . biocal showed the lowest solubility ( 0.72% ) , after water immersion for 1 week , and differed significantly from the chemically activated cements . dycal showed intermediary solubility ( 4.21% ) and hidro c presented the highest solubility ( 7.65% ) . the water sorption values showed correlation with the solubility values : the higher the water sorption , the greater the solubility for the evaluated materials . according to tam , et al.15 , high strength and low solubility are desirable for any base or lining material . a strong base material is needed to support the overlying restoration and the subsequent occlusal forces acting upon it during clinical function . some reduction observed in compressive strength may be attributed to dissolution or water sorption during storage . moreover , marginal infiltration may influence on liners hardness , which reinforces the need for studies related to their physical properties . this study was aimed at elucidating essential values for the evaluation of the quality of each employed material , which is of important clinical applicability . in fact , lining and base materials have to be resistant to dissolution in water , organic solvents and acid - etching solutions , in order to maintain their pulp protective effect16 . in addition , dissolved and smeared calcium hydroxide may contaminate acid - etched enamel , and produce an inferior bond , which is not desirable10 . the choice for the three kinds of cements here evaluated was based on the fact that dycal and hidro c are the most commonly used conventional lining materials , in the clinical practice . biocal was used in this study because it is a resin - based calcium hydroxide cement , easily found on the market . its main advantage , according to the manufacturer , is to present less solubility and water sorption , which improves its physical properties and , consequently , increases its longevity when it is used under restorations . water sorption and solubility tests were applied according to the ada 's # 8 specification , though with few alterations to meet the objectives of this study . however , the results obtained in laboratorial studies must be carefully applied to the clinical conditions since calcium hydroxide cement bases are significantly more soluble in distilled water than in simulated dentinal fluid or saliva used in other studies . likewise , the length of time specified by ada solubility test ( 1 week ) does not seem to be adequate for testing lining materials , as they continue to dissolve in the next 3 months3 . although pulp - capping materials look similar as far as mixing and composition are concerned , in that they are essentially calcium hydroxide and an ester of salicylic acid , posser , et al.12 have shown that there are several important differences in their components . the present study showed that the differences in the basic composition of the evaluated cements , that is , the presence or absence of resin particles , determined and influenced positively biocal behavior , a resin - modified light - cured material . this cement ( biocal ) showed lower solubility and less water sorption , after 1-week immersion in distilled water when compared with chemically activated cements ( dycal and hidro c ) . similar results have been reported by burke and watts2 , where resin - based lining materials proved to have better resistance than conventional calcium hydroxide cements , even if further clinical properties of those materials , such as their polymerization shrinkage , still need to be investigated . it is important to emphasize that the results of the present study can not be extrapolated to conditions others than the ones described here . nevertheless , if a base material is to be selected for its biological properties , it should present some degree of dissolution at the vital dentin - base interface . if this material is relatively insoluble , ion exchange with the odontoblastic layer may be hindered , and consequently the amount of secondary dentin is reduced and its main indication is questionable3 . on the basis of this study , it may be concluded that : 1- biocal absorbed less water and is less soluble than the other evaluated cements ; 2- hidro c showed the highest water sorption and solubility rates ; and 3- there were significant differences among the tested materials .
objectives : calcium hydroxide cements have been largely used in deep cavities due to their abilities to stimulate dentin formation . however , their resistance can be relatively low and their solubility relatively high , in many instances . 
 this study evaluated water sorption and solubility of different calcium hydroxide cements , in order to show alterations that may reduce their effectiveness.material and methods : five discs ( 20 mm in diameter and 1.5 mm thick ) of three different materials ( biocal , dycal and hidro c ) were prepared with the aid of a ring - shaped metallic matrix . after being stored at 37c for 24 h , 
 the discs were weighed on a precision weight scale , dehydrated and weighed again . immediately after weighing , discs were stored for a week in 50 ml of distilled water at 37c and , then , weighed again , dehydrated and submitted to a new weighing . 
 the loss of soluble material and its water sorption was obtained from the difference between the initial and the final dry mass of each disc , after 1 week of immersion in water . 
 data were analyzed for significant differences by two - way anova and tukey 's test ( p<0.05).results : mean water sorption values ( g )  standard deviation and percentage ( % ) , for each evaluated cement , were : biocal ( 0.006  0.001 / 2.15 ) ; dycal ( 0.016  0.004 / 5.49 ) ; and hidro c ( 0.025  0.003 / 8.27 ) . mean solubility values ( g )  standard deviation and percentage ( % ) , for each evaluated cement , were : biocal ( 0.002  0.001 / 0.72 ) ; dycal ( 0.013  0.004 / 4.21 ) ; and hidro c ( 0.023  0.004 / 7.65).conclusions : biocal absorbed less water and was less soluble than the other evaluated cements ; hidro c exhibited the highest water sorption and solubility values ; and there were significant differences among all evaluated experimental groups .