BACKGROUND OF THE INVENTION  
       [0001]     During the manufacture of semiconductor devices arranged in arrays on wafer substrates, the wafers are subjected to various chemical treatments. The treatments are in the form of a number of process steps that the wafers undergo during the formation of devices, including the formation of, processing of, and removal of, layers, photolithography processes, and the like. Following certain steps, extraneous particles can remain on the substrate, which can have an adverse effect on subsequent processes. In contemporary fabrication techniques, the substrates are rinsed and dried to remove such particles.  
         [0002]     For rinsing the wafers, it is common to use deionized water (DI) or a commercial cleaning solution such as SC1. When drying the substrate, isopropyl alcohol (IPA) is commonly used. However, IPA-based drying processes commonly leave particles and watermarks on the substrates. To improve the IPA-based drying process, a drying technique referred to as the Marongoni technique, has become popular.  
         [0003]     In the Marongoni technique, the wafers are slowly lifted out of the DI bath, or the DI bath is slowly drained. At this time, the exposed wafers are immersed in an IPA vapor. Since the concentration of the IPA vapor is highest at the interface with the DI bath, the resulting surface tension of the water is low in this region. This results in a phenomenon referred to as Marongoni flow of the DI water bath away from the wafer surfaces, thereby drying the wafer surfaces. While the Marongoni approach is somewhat effective for removing particles from the wafers, because the slow drain procedure drastically reduces process throughput. For example, the drain time may be on the order of 225 seconds for a 12 inch wafer. In addition, watermarks can remain on the substrate following a Marongoni flow procedure.  
         [0004]     To improve the effectiveness of the removal of particles and watermarks by the IPA vapor, heated nitrogen gas N 2  can also be introduced into the process chamber. This technique is disclosed in U.S. Pat. No. 6,328,809, the content of which is incorporated herein by reference. With reference to  FIG. 1 , in this approach, the IPA vapor is transported into a wafer process chamber using a source of heated nitrogen gas. Referring to  FIG. 1 , nitrogen from a nitrogen gas source N 2  flows through valve  11 , is heated at heater  12 , and flows through valve  15 A into a tank  10  containing IPA solution. The IPA solution is partially heated into a vapor within the tank by heater  14 . The pressure of the heated nitrogen gas forces the combined nitrogen and IPA gases to flow through valve  15 C and into the process chamber  20 . The combined IPA/N 2  gas is introduced into the process chamber  20  to carry out an IPA decontaminating step. During this step, valve  15 B is closed. Following this, heated N 2  gas flows directly into the process chamber by closing valves  15 A and  15 C and opening valve  15 B in a purge step, in order to volatize any condensed IPA remaining on the wafers.  
         [0005]     To ensure the removal of particles and watermarks, the ratio of nitrogen gas to IPA gas in the process chamber is a critical factor during the IPA decontaminating step, since the ratio is closely correlated with device yield. However, control over this ratio is limited in the conventional approaches, since the nitrogen gas is used exclusively as a transport medium for the IPA gas during the decontaminating procedure.  
       SUMMARY OF THE INVENTION  
       [0006]     The present invention is directed to a system and method for rinsing, decontaminating and drying semiconductor wafers in a manner that improves yield by providing more advanced control of the ratio of drying fluid to cleaning fluid, for example the ratio of N 2  vapor to IPA vapor. In addition, a quick drain process is employed to improve process throughput, and to further improve particle and watermark removal during the rinsing, decontamination, and drying steps.  
         [0007]     In one aspect, the present invention is directed to a system for processing semiconductor wafers. A first inlet for a first supply of drying fluid is provided. A second inlet for a second supply of drying fluid is also provided. The rate of supply of the second supply of drying fluid is independent of that of the first supply of drying fluid. A decontaminating fluid tank stores a supply of decontaminating fluid, the decontaminating fluid tank having an inlet for receiving the second supply of drying fluid, and having an outlet for supplying decontaminating fluid at a rate that is based on the rate of supply of the second supply of drying fluid. A process chamber houses the semiconductor wafers to be cleaned and dried. The process chamber includes an inlet for simultaneously receiving the first supply of drying fluid and the supply of decontaminating fluid.  
         [0008]     The first supply of drying fluid and second supply of drying fluid comprise, for example, nitrogen gas. A first heater may be provided for heating the first supply of drying fluid between the first inlet and the process chamber. A second heater may be provided for heating the second supply of drying fluid between the second inlet and the decontaminating fluid tank.  
         [0009]     A third heater may be coupled to the decontaminating fluid tank for heating the decontaminating fluid in the tank. The decontaminating fluid in the tank is partially heated by the third heater from a liquid into a vapor and the second supply of drying fluid drives the decontaminating fluid vapor through the outlet of the decontaminating fluid tank. The inlet of the decontaminating fluid tank may include a first inlet for receiving the second supply of drying fluid at a level below the level of the liquid and a second inlet for receiving the second supply of drying fluid at a level above the level of the liquid.  
         [0010]     A fourth heater may be coupled to a line in turn coupled to the inlet of the process chamber for heating the first supply of drying fluid and the supply of decontaminating fluid prior to their release into the process chamber.  
         [0011]     The first supply of drying fluid and the supply of decontaminating fluid received at the process chamber are preferably in a vapor state.  
         [0012]     A coupling tube may be provided for selectively coupling the first supply of drying fluid to the decontaminating fluid tank. In addition, a coupling tube may be provided for selectively coupling the second supply of drying fluid directly to the process chamber. Also, a coupling tube may be provided for selectively coupling the first inlet to the second inlet.  
         [0013]     The process chamber further comprises a drain, and a buffer tank is coupled to the drain of the process chamber. In one embodiment, the drain comprises a plurality of drains, and the plurality of drains are coupled to the buffer tank. The plurality of drains are, for example, of a width to ensure rapid draining of the process chamber, for example within a time period less than about 50 seconds, or, for example, within a time period ranging between about 7 and 17 seconds. The multiple drains are spaced apart in the process chamber to ensure that a top surface of a fluid to be drained from the process chamber remains level as the process chamber is drained. The buffer tank is preferably of a volume that is greater than or equal to the volume of the process chamber.  
         [0014]     A first supply rate controller is provided for controlling the rate of supply of the first drying fluid and a second supply rate controller is provided for controlling the rate of supply of the second drying fluid, the first and second supply rate controllers being independent of each other such that the rate of supply of the first drying fluid and the rate of supply of the second drying fluid are independent relative to each other.  
         [0015]     The process chamber may further comprise a plurality of exhaust ports distributed in the process chamber to provide for laminar flow of the decontaminating fluid and the drying fluid in the process chamber.  
         [0016]     In another aspect, the present invention is directed to a method for processing semiconductor wafers. A first supply of drying fluid is provided and a second supply of drying fluid is also provided. The rate of supply of the second supply of drying fluid is independent of that of the first supply of drying fluid. A supply of decontaminating fluid is stored in a decontaminating fluid tank. The decontaminating fluid tank has an inlet for receiving the second supply of drying fluid, and has an outlet for supplying decontaminating fluid at a rate that is based on the rate of supply of the second supply of drying fluid. The first supply of drying fluid and the supply of decontaminating fluid are simultaneously supplied to a process chamber to decontaminate semiconductor wafers contained therein.  
         [0017]     Prior to simultaneously supplying the first supply of drying fluid and the supply of decontaminating fluid to the process chamber, rinsing fluid, for example DI water, is supplied into the process chamber containing the semiconductor wafers for rinsing the semiconductor wafers. The rinsing fluid is then rapidly drained from the process chamber, for example into a buffer tank.  
         [0018]     In a preferred embodiment, the rinsing fluid is completely drained prior to simultaneously supplying the first supply of drying fluid and the supply of decontaminating fluid to the process chamber.  
         [0019]     Following simultaneously supplying the first supply of drying fluid and the supply of decontaminating fluid to the process chamber, a drying fluid, for example nitrogen gas, is supplied into the chamber for drying the semiconductor wafers.  
         [0020]     Throughout the present specification and claims, the term “fluid” is used herein in a manner consistent with its historical definition, and therefore includes any non-solid form of matter, for example gases, vapors, and liquids. 
     
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0021]     The foregoing and other objects, features and advantages of the invention will be apparent from the more particular description of preferred embodiments of the invention, as illustrated in the accompanying drawings in which like reference characters refer to the same parts throughout the different views. The drawings are not necessarily to scale, emphasis instead being placed upon illustrating the principles of the invention.  
         [0022]      FIG. 1  is a schematic block diagram of a conventional cleaning and drying system for cleaning and drying semiconductor wafers.  
         [0023]      FIG. 2  is a block diagram of a cleaning and drying system, in accordance with the present invention.  
         [0024]      FIG. 3  is a schematic block diagram of a first cleaning and drying system for cleaning and drying semiconductor wafers in accordance with the present invention.  
         [0025]      FIG. 4  is a schematic block diagram of a second cleaning and drying system for cleaning and drying semiconductor wafers in accordance with the present invention.  
         [0026]      FIG. 5  is a block diagram of a process chamber draining system in accordance with the present invention.  
         [0027]      FIG. 6  is a chart illustrating remanent particle density as a function of the rate of flow of nitrogen vapor, in accordance with the present invention.  
         [0028]      FIG. 7  is a chart illustrating remanent particle density as a function of drain time, in accordance with the present invention.  
         [0029]      FIG. 8  is a chart that illustrates the selection of optimal flow rates for the carrier nitrogen vapor and the purge nitrogen vapor, in accordance with the present invention.  
         [0030]      FIG. 9  is a flow diagram of a wafer cleaning and drying process, in accordance with the present invention. 
     
    
     DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS  
       [0031]      FIG. 2  is a block diagram of a cleaning and drying system, in accordance with the present invention. The system includes a process chamber  100  within which semiconductor wafers are rinsed, decontaminated, and dried, a deionized (DI) water source  101  for rinsing the wafers, and an isopropyl alcohol (IPA) source  102  and nitrogen source  104  for decontaminating and drying the wafers. Following the rinsing step, waste rinse fluid from the process chamber  100  is rapidly drained through multiple drain lines  218  (described below) into a buffer tank  220  using a “quick-drain” process. The quick-drain process is described in further detail below. The buffer tank releases the waste rinse fluid through a drain line  224 , and the waste fluid is treated in a waste facility. In addition, organic gases, for example IPA gases, are exhausted from the process chamber, for example, at exhaust ports  217  (described below), and treated at a scrubber  225  to prevent fire and release of toxins.  
         [0032]     The following process is described below with additional reference to the flow diagram of  FIG. 9 . To initiate the cleaning and drying process, the wafers to be processed are loaded into the process chamber  100 . A rinsing operation is performed to remove process chemicals, for example etch chemicals. DI water provided by source  101  flows into the chamber prior to, or following, placement of the wafers so as to submerge the wafers. In one example, the DI water rinse fluid comprises hydrofluorine (HF)-buffered DI water. Alternatively, commercial cleaning solution, such as SC1, maybe used. The DI water flow continues, causing the process chamber to overflow, thereby thoroughly rinsing the surfaces of the wafers (step  402 ).  
         [0033]     Following this, the DI water is rapidly drained from the process chamber  100 , using the “quick-drain” apparatus described below, for example the draining tubes placed in less than about 50 seconds, and preferably within about 7-17 seconds (step  404 ). To accommodate the quick-drain, the DI water is released via a plurality of wide, evenly distributed, drain apertures into a buffer tank  220  that lies below the process chamber  100 . The buffer tank  220  temporarily holds the waste fluid until it can be properly disposed via drain line  224 .  
         [0034]     In the decontamination step, the lid of the process chamber  100  is closed, gas exhaust ports of the chamber are opened (step  406 ), and a flow of heated IPA vapor from source  102  is delivered to the process chamber  100  to initiate the wafer drying process, and to further remove contaminants, for example contaminants in the form of particles, from the surfaces of the wafers (step  408 ). In one example, the heated IPA vapor  102  flows for about 90 seconds. The IPA vapor is delivered to the process chamber  100  using nitrogen  104  as a carrier vapor. In the present invention, during the decontamination step, the flow rate of nitrogen vapor is precisely controlled, in order to provide the process chamber environment with an optimal IPA-to-nitrogen ratio, which, in turn, provides for optimal cleaning, drying and removal of watermarks from the wafers.  
         [0035]     In one example, the flow rate of nitrogen vapor is controlled by providing, in addition to the “carrier” nitrogen vapor flow used to drive the IPA vapor, a second, independent source of heated nitrogen gas into the process chamber  100  to ensure the proper IPA-to-nitrogen ratio in the chamber  100  (step  408 ). This second source of nitrogen is referred to below as the “purge” nitrogen vapor, since the second source can optionally later be used to purge the process chamber during the subsequent drying step. It should be noted, however, that the first source, or “carrier” nitrogen source, can also be used for the subsequent drying step, as described below. It has been determined that rapid draining of the DI water bath, during the rinsing step, combined with an optimized IPA-to-nitrogen ratio during the decontamination step, lead to optimal removal of particles from the wafers, as described below.  
         [0036]     The IPA decontamination vapor of the decontamination step may be introduced during the quick-drain of the rinsing fluid, or, preferably, is introduced following completion of the quick-drain procedure. Experimental data indicates that IPA introduction following completion of the quick-drain procedure results in fewer particles remaining on the wafers. During the decontamination step, the plurality of drain lines from the process chamber  100  to the buffer tank  220  remain open. In addition, multiple gas exhaust lines  217  in the process chamber, described in further detail below, are open during this step. The operation of the multiple gas exhaust lines is described in further detail below.  
         [0037]     Following this, heated nitrogen vapor, for example from the second nitrogen vapor source, is sprayed onto the wafers to dry the wafers (step  410 ). In one example, the nitrogen flow is activated for approximately 300 seconds. Again, during this step, the plurality of drain lines from the process chamber  100  to the buffer tank  220 , as well as the gas exhaust lines, remain open in order to maintain uniform pressure in the chamber and to remove IPA from the chamber at the same time.  
         [0038]     Following this, the process chamber exhaust lines and drain lines are closed. The lid of the chamber is then opened, and the cleaned and dried wafers are removed.  
         [0039]      FIG. 3  is a schematic block diagram of a first cleaning and drying system for cleaning and drying semiconductor wafers in accordance with the present invention. In this embodiment, a first flow of nitrogen is provided by a first nitrogen source  104 A. The rate of flow of the first nitrogen source  104 A is controlled by a first mass flow controller (MFC)  183 , in which an electrical signal is used to maintain a suitable flow rate.  
         [0040]     The controlled flow of the first nitrogen source is heated by a first heater  106 A to an appropriate temperature. A second flow of nitrogen is provided by a second nitrogen source  104 B. The rate of flow of the second nitrogen source  104 B is controlled by a second mass flow controller (MFC)  182 . The controlled flow of the second nitrogen source is heated by a second heater  106 B to an appropriate temperature. An IPA source  102  is coupled to an IPA tank  120 . A filter  126  is provided for purifying the IPA solution prior to entry into the tank  120 . Valve  185  enables the flow of IPA solution to the IPA tank  120 .  
         [0041]     IPA solution in liquid form pools in the bottom of the IPA tank  120 . A heater  122  in the base of the IPA tank  120  vaporizes a portion of the IPA solution to generate an IPA vapor that resides above the solution.  
         [0042]     As stated above, during an IPA-based decontaminating procedure, the IPA vapor located in the IPA tank  120  is transported into the process chamber  100  by the first flow  104 A of heated nitrogen gas, i.e. the “carrier” nitrogen supply. During this step, valves  112  and  116  are open and valve  114  is closed. The nitrogen gas heated by the heater  106 A flows through valve  112  into the IPA tank  120 , where it reacts with the IPA vapor in the tank  120 . The IPA vapor is then transported by the incident nitrogen vapor through valve  116 , into the process chamber  100 . An optional line heater  130  heats the combined nitrogen and IPA vapor supplied at line  191  to a predetermined temperature prior to entry into the process chamber  100 . The line heater comprises, for example, a quartz plate/heating coil/quartz plate configuration which envelops the gas line. The line heater  130  maintains the temperature of the gases entering the process chamber  100 , in order to increase the reliability of the semiconductor manufacturing process.  
         [0043]     At the same time, during the IPA-based decontaminating procedure, in order to precisely control the IPA-to-nitrogen ratio of the decontaminating vapor entering the process chamber  100 , a second source of heated nitrogen supplied at line  193  from the second nitrogen source  104 B is provided, referred to above as the “purge” nitrogen source. As stated above, the rate of flow of the second source of nitrogen is precisely controlled, for example by the second MFC  182 , in order to ensure the proper ratio. The vapor provided by the second source  104 B at line  193  is also heated by the line heater  130 , where it is mixed with the combined nitrogen/IPA vapor from line  191 . Together, the first and second vapor sources arriving via lines  191  and  193  are provided to the process chamber  100  via line  195 .  
         [0044]     In a preferred embodiment, the line heater  130  heats the applied vapor such that it is released at line  195  at a temperature of about  130 C. At the same time, the first heater  106 A operates to heat the first nitrogen gas source  104 A to a temperature of about 100C-120C, the second heater  106 B operates to heat the second nitrogen gas source  104 B to a temperature of about 130C-150C, and the IPA tank heater  122  operates to heat the IPA solution in the tank to a temperature of about 50C to 70C. The operating temperature of the first heater  106 A is preferably lower than the operating temperature of the second heater  106 B, because a lower temperature is required for precisely controlling the delivery rate of the IPA vapor from the IPA tank  120 .  
         [0045]     As stated above, during the drying step, heated nitrogen gas flows directly into the process chamber  100 , for volatizing any condensed IPA remaining on the wafers. During this step, valves  112  and  116  are closed, and valve  114  is open. The second “purge” nitrogen source  104 B may optionally be used in conjunction with, or instead of, the first nitrogen source  104 A for this step.  
         [0046]     As an optional entry configuration for the heated nitrogen gas into the IPA tank, dual entry ports  124 A,  124 B may be provided. The first port  124 A lies above the surface of the IPA solution in the tank, to serve as a pressurized transport mechanism for the IPA vapor lying above the solution surface, as described above. The second port  124 B enters the IPA tank below the surface of the IPA solution, and mixes, or bubbles, directly with the IPA solution, to further activate the reaction with the IPA solution. In this manner, the interaction of the IPA solution with the nitrogen carrier vapor is enhanced.  
         [0047]      FIG. 4  is a schematic block diagram of a second cleaning and drying system for cleaning and drying semiconductor wafers in accordance with the present invention. This embodiment is similar in structure and performance to those of the first embodiment described above in connection with  FIG. 3 . However, in this embodiment, an additional flow line  134  is connected between the line  193  providing the heated second nitrogen source and the entry ports  124 A,  124 B of the IPA tank  120 . This flow line  134  allows the second nitrogen source  104 B to serve as a “carrier” vapor source for the IPA tank, for example to allow for servicing of the first MFC  183  or the first heater  106 A without having to disrupt system operation. In this case, valve  132  is closed, valve  112  is closed, and valve  128  is open. At the same time, the first nitrogen source  104 A may be directly applied to the process chamber  100 , by opening valve  114  to initiate flow via line heater  130 , after being mixed with the IPA/nitrogen vapor mixture at line  191 . The roles of the first and second nitrogen sources  104 A,  104 B are thus temporarily reversed in this example to allow for servicing of the first MFC  183  and/or the first heater  106 A.  
         [0048]     In addition, this second embodiment provides an optional line  187  and related valve  187 A that combines the first and second nitrogen sources  104 A,  104 B. It should be noted that while the first and second nitrogen sources  104 A,  104 B are illustrated as different, independent sources, they may, in fact comprise a common source that has two outlets, the flow of each outlet being independently controlled, for example by the first and second MFC&#39;s  183 ,  182 . In this case, the common source should maintain a pressure great enough to source the combined flow rate of the MFCs  183 ,  182 .  
         [0049]      FIG. 5  is a block diagram of the process chamber  100 , including a draining system that provides for rapid draining of the chamber in accordance with the present invention. The process chamber  100  includes a bath  210  capable of processing multiple wafers, for example 50 semiconductor wafers  212 , at a time. The wafers are supported by support  214 . At a bottom region  216  of the bath  210 , a plurality of drain openings  219  are provided. A plurality of exhaust port openings  217  are also provided. The respective drain openings  219  are relatively wide in cross section to allow for rapid draining of fluid, for example, the DI water fluid, from the bath  210 . The drain openings  219  are coupled to multiple drain lines  218 , which transport the rapidly discharged fluid into a buffer tank  220 . The buffer tank preferably has a volume at least as large as the volume of the bath  210 , so that it can receive the entire content of the bath liquid all at once, without hindering the flow of liquid.  
         [0050]     The multiple drain openings  219  and multiple drain lines  218 , are preferably distributed across the lower side  216  of the bath  210 . This configuration ensures that, during draining, the fluid being drained remains level and flat as it is drained, in turn ensuring the same exposure time for the different wafers being processed in the bath, irrespective of where the wafers are located in the bath  210  relative to the drain outlet  219 . This feature overcomes a funneling phenomenon that would otherwise occur if a single drain were to be used, which would lead to different exposure times for the different wafers, the exposure times corresponding to their positions relative to the single drain location.  
         [0051]     Similarly, the multiple exhaust ports  217  are included in the bath for ensuring an even distribution, i.e. laminar flow, of the decontaminating and drying vapors in the bath  210 . Following the quick drain procedure, when the IPA and N 2  gases are introduced for the decontamination step, the multiple exhaust ports  217  are opened to allow for the even flow of decontamination vapors across the wafers. This avoids the problem associated with a single exhaust port, which would tend to concentrate the vapor flow in certain regions of the bath, for example due to eddy currents. In a preferred embodiment, the exhaust ports  217  remain open during the decontamination step and the drying step, and are optionally open, when needed, during the quick-drain step.  
         [0052]     In this manner, the present invention increases semiconductor fabrication productivity. To increase productivity, the drain time of DI water is aggressively shortened by use of the quick-drain procedure. Watermarks remaining on the wafers as a result of the quick drain process are then efficiently removed by precisely controlling the ratio of nitrogen gas to IPA gas during the decontamination procedure. In this manner, process throughput is enhanced, in a manner that lends itself well to high process quality.  
         [0053]      FIG. 6  is a chart illustrating remanent particle density as a function of the rate of flow of nitrogen vapor, in accordance with the present invention. An experiment was conducted to determined the effectiveness of the decontamination step where the second, independent heated nitrogen source  104 B was included, for improving control over the IPA-to-nitrogen ratio in the decontaminating fluid introduced into the process chamber  100 . In this experiment, the first heater  106 A, second heater  106 B, and line heater  130  were set at a temperature of 130C. The IPA tank heater  122  was set at a temperature of 65C. The chamber exhaust pressure was set at 75 mmH 2 O.  
         [0054]     In a first experiment, represented by plot I of  FIG. 6 , the first nitrogen source  104 A was activated, for driving the IPA vapor, and the second nitrogen source  104 B was dormant. In this case, optimal flow rate of the first nitrogen source  104 A is determined to be at the minimum of the curve, or at about 50 liters per minute (LPM), resulting in over 100 particles remaining per 300 mm wafer.  
         [0055]     In a second experiment, represented by plot II, the first nitrogen source  104 A and second nitrogen source  104 B were both activated, the first source  104 A being set at 20 LPM for driving the IPA vapor, and the second source  104 B for supplying additional nitrogen into the process chamber  100  for improved control over the IPA-to-nitrogen ratio in the chamber. In this case, the minimum of the plot II curve fell over a range of about 40-70 LPM flow of the second nitrogen source  104 B, for which particle density was on the order of less than 30 particles remaining per 300 mm wafer.  
         [0056]      FIG. 7  is a chart illustrating remanent particle density as a function of drain time, in accordance with the present invention. Assuming the conditions of the above experiment, with the first nitrogen source  104 A operating at a flow rate of 20 LPM, and with the second nitrogen source  104 B operating at a flow rate of 50 LPM, and assuming 140 cc of IPA being used for the decontamination step, remanent particle density was determined as a function of drain time. It can clearly be seen in the chart that as drain time is reduced, the remanent particle density improved. In the range of 7-17 seconds of drain time, particle density was on the order of less than 20 particles remaining per 300 mm wafer.  
         [0057]      FIG. 8  is a chart that illustrates the selection of optimal flow rates for the first “carrier” nitrogen source  140 A and the second “purge” nitrogen source  140 B, in accordance with the present invention. In region  308  of the chart, the carrier nitrogen source is at too small of a flow rate to properly dry the wafers. In region  310  of the chart, too much carrier nitrogen is present, and, as a result, too much IPA vapor is presented to the wafers, resulting in IPA gel formation on the wafers and in the process chamber. Regions  302  and  304  of the chart indicate preferred combinations of carrier nitrogen and purge nitrogen levels that lead to preferred IPA-to-nitrogen ratios in the process chamber. Arrow  303 , for example, indicates a carrier nitrogen flow rate of 10 LPM and a purge nitrogen flow rate of 100 LPM. An optimal condition exists at the intersection of the charts at point O  306 , where the carrier nitrogen flow rate is 20 LPM and the purge nitrogen flow rate is 50 LPM.  
         [0058]     While this invention has been particularly shown and described with references to preferred embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made herein without departing from the spirit and scope of the invention as defined by the appended claims.
A system and method for cleaning and drying semiconductor wafers improves device yield by providing more advanced control of the ratio of drying fluid to cleaning fluid, for example the ratio of N 2 vapor to IPA vapor. In addition, a quick drain process is employed to improve process throughput, and to further improve particle and watermark removal during the cleaning and drying steps.