shown by the cyclic compression test in Fig 5c and Movie S3. Interestingly, the stress-compression profile reveals two distinct regimes. At compressive strains below ~30%, the compressive stress increases nearly linearly with strain and corresponds to an apparent elastic modulus of 18 kPa at 𝜖 𝑐 = 30%. Above 30% strain, the stress begins to increase more rapidly with a maximum stress of 325 kPa reached at 60% strain. When comparing the loading and unloading cycles, the printed gyroid exhibits a hysteresis associated with 25% energy dissipation (inset, Fig. ). This energy dissipation is primarily attributed to the breakage and reformation of the reversible hydrogen bonds.