Despite the resolution limitations of this technique, the analysis suggests that initial defects and early-cycle cracks act as nucleation points for further cracking, often forming persistent main structures. After discharge, primary particles appear to fail at reconnecting, leaving grain boundaries as recurring weak points. Higher-resolution imaging is needed to confirm these findings.