Finally, polymers with one repeat unit pendent chains (MEMA) were varied between 30 and 50 mol% control monomer and reacted in the presence of EDA. Increasing the control monomer ratio from 30 to 50% slightly decreased to rate at which the material crosslinked and the final modulus, from 10 5 Pa at 30 and 40 mol% control monomer to just above 10 4 Pa at 50 mol% control monomer (Figure ). As expected, the small size of the MEMA comonomer did not contribute significantly to suppressing the crosslinking kinetics of the crosslinking polymers.