A small amount of MOF powder was placed in alumina crucibles and heated from 30 to 800 °C at a constant rate of 10 °C min⁻¹ under a synthetic air atmosphere. To account for the buoyancy effect and obtain precise sample mass measurements, a baseline measurement using an empty crucible under identical experimental conditions was subtracted from the recorded data.