The large anisotropic volume changes of Ni-rich cathode materials during cycling result in the mechanical degradation at the cathode/solid-electrolyte interface, which leads to the increase of electrode impedance and capacity loss . This phenomenon is compounded by the substantial formation of crystal defects within the cathode particles, to reduce the stress magnitude and accommodate the large compositional strain.