In addition, Mn 2+ formation is frequently observed for n-type defects, suggesting a strong driving force for Mn 3+ to undergo disproportionation reactions. The atomic chemical potential values can be found in Table . Two variant approaches assuming certain defects are "frozen in" during synthesis were adopted to simulate defect behaviours at room temperature (300 K).