Maps obtained from the Rietveld analysis of the NMC532 phases are shown in Figure and Supplementary Figure . The crystallite sizes obtained with the three different methods on the top row of Figure indicate the crystallite sizes calculated from the ParallaxNet reconstructed volume are larger than both FBP methods with 180 and 360 °scans respectively. The average crystallite sizes raised from ca. 91 nm (for FBP with 180 °scans) and 92 nm (for FBP with 360 °scans) to 137 nm (for the ParallaxNet), which also supports the conclusion we drew from visual inspection: the diffraction peaks are sharper and narrower than those produced by conventional methods. The R wp maps of the Rietveld analysis are shown in Supplementary Figure . The lattice parameter maps of the NMC532 phase also indicate that the ParallaxNet can correctly reconstruct the evenly distributed lattice parameter maps which aligns with the FBP with 360 °scan. The peak shifting artefact in the images reconstructed by the FBP with 180 °scan range has been effectively eliminated by ParallaxNet. The distribution of the lattice parameters of the NMC532 is presented in Supplementary Figure .