However, the ultimate failure strain of 5 wt.% GNP-coated composite was higher than untreated and 1 wt.% GNP-coated composite (Table ). In glass-carbon/epoxy hybrid composites, crack initiation occurs after carbon fibre failure at the matrix site and spreads rapidly due to the absence of mechanical interlocking between the fibres and matrix.