Secondly, our glass transition temperatures reproduce the expected monotonically increasing trend with increasing cross-linking extents, while also lying close to experimental values measured at similar curing temperatures. This result emerged from determining the master curve for the density-temperature relation for all curing intensity. The consequent evaluation of T g as a function of curing is then robust against deviations from hyperbolic trend of any density data sets and the finite temperature window explored in the simulations.