Table is the result for the tetragonal phase of Na 3 PS 4 (mp-28782). This is particularly similar to the cubic phase with a structural distortion at the Na sites. Its space group P 42 1 c was retrieved as the first scored one. The top-2 scored local atomic environments were retrieved correctly, but the following three retrievals were wrong. This error is the same type that is considered to have come from the complex sentence structure and our relatively simple text inputting. Two updated descriptions were found on the Materials Project, which were added in the The connected geometries were missed in the above analysis. We give additional results for Na 3 PS 4 with adding all the full patterns of polyhedral connections. For the cubic phase (Table ), "This crystal has bondings to form distorted [POLYHEDRA] trigonal pyramids that share corners with three equivalent [POLYHEDRA] tetrahedra" was retrieved as the second scored next to the first scored "[NONMETAL] is bonded in a tetrahedral geometry". The other retrievals are just similar to the trigonal pyramids, like tetrahedra, and seem not be improved compared to Table . For the tetragonal phase (Table ), "This crystal has bondings to form distorted [POLYHEDRA] tetrahedra that share corners with four equivalent [POLYHEDRA] pentagonal pyramids and an edge-edge with one [POLYHEDRA] tetrahedra" was retrieved as the first scored, and "This crystal has bondings to form distorted [POLYHEDRA] pentagonal pyramids that share corners with eight equivalent [POLYHEDRA] tetrahedra" as the second scored, both of which grasp the connected geometries to some extent, but not accurately up to the detailed numbers of connections.