Ultimately for ML (Ni) when tested with a 25N load, coating failure begins when there is an exhaustion of nickel metal to sequester the oxygen during sliding. At this point, the surfaces of the tribofilm become oxidized and mechanically compromised, and suffer the same tribological failure processes as seen in ML (Cu) sliding.