A slightly lower hardness of h-C 6 and rh-C 3 compared to diamond (both cubic and hexagonal) is observed for both models (Table ). On the other hand, hardness of these phases is much higher than hardness of the vast majority of recently predicted carbon allotropes (C 14 , C 16 , C 24 , C 36 , etc.) .